This product, widely used in construction, automotive, shipbuilding, and electrical products, is an adhesive that uses halogen-free flame retardants.
It exhibits excellent adhesion and a transparent coating surface after drying.
It exhibits excellent adhesion and a transparent coating surface after drying.
| Product Name | Solid Content(%) | Viscosity(CPS) | Substrate | Coating Amount(㎛) | Initial Adhesion(kgf/25mm) | Room Temperature Adhesion(kgf/25mm) | Remarks |
|---|---|---|---|---|---|---|---|
| YEF-1000 | 60±1 | 6500±500 | OPP 40㎛ | 40 | 1.3±0.1 | 1.4±0.1 | 110≥ |
| YJ-100-5 | 67±1 | 6500±500 | OPP 40㎛ | 70 | 0.9±0.3 | 1.2±0.3 | 120℃ |
YEF-1000
비할로겐난연점착제로 난연성및 점착력이 우수하다.
제품명Mode |
난연성 아크릴점착제(YEF-1000) |
|||
|---|---|---|---|---|
재질Grade Material |
아크릴에멀젼 점착제 |
규격Spec |
MS 715-71 | |
시험항목Test Items |
단위 | 결과 | 시험방법 | |
| 기재 | 40㎛ OPP film | |||
| 고형분 | % | 60±1 | 3.2 | |
| 점도 | cps ／25℃ | 6500±500 | 3.3 | |
| 내열성 | ℃ | 110≥ | 3.4 | |
| 도포량 | ㎛ | 40 | 3.5 | |
| 초기박리강도 | (Kgf/25mm) | 1.3±1 | 3.6 | |
| 상온박리강도 | (Kgf/25mm) | 1.4±1 | 3.7 | |
- 숙성조건 : 상온 X 1일
- 초기접착력: 부착후 30분 경과 후 180° Peel test(시험속도 :300mm/min)
- 후기접착력: 부착후 60℃ X 24시간 경과 후 180° Peel test(시험속도 :300mm/min)
- 내열성:500g 추를 이용하여 40℃부터 3℃/5분씩 승온하여 150℃까지 실행
YJ-100-5
비할로겐난연점착제로 난연성및 점착력이 우수하다.
제품명Mode |
난연성 아크릴점착제(YJ-100-5) |
|||
|---|---|---|---|---|
재질Grade Material |
아크릴에멀젼 점착제 |
규격Spec |
MS 715-71 | |
시험항목Test Items |
단위 | 결과 | 시험방법 | |
| 기재 | 40㎛ OPP film | |||
| 고형분 | % | 67±1 | 3.2 | |
| 점도 | cps ／25℃ | 6500±500 | 3.3 | |
| 내열성 | ℃ | 120℃ | 3.4 | |
| 도포량 | ㎛ | 70 | 3.5 | |
| 초기박리강도 | (Kgf/25mm) | 0.9±0.3 | 3.6 | |
| 상온박리강도 | (Kgf/25mm) | 1.2±0.3 | 3.7 | |
- 숙성조건 : 상온 X 1일
- 초기접착력: 부착후 30분 경과 후 180° Peel test(시험속도 :300mm/min)
- 후기접착력: 부착후 60℃ X 24시간 경과 후 180° Peel test(시험속도 :300mm/min)
- 내열성:500g 추를 이용하여 40℃부터 3℃/5분씩 승온하여 150℃까지 실행